Analisis Keretakan pada Sambungan Las antara Pipa ASTM A106 dengan Globe Valve
Abstract views: 495 | pdf downloads: 491
Abstract
Crack failure often occurs in piping installations, especially in the welding area which can be caused by excessive stress or corrosion of the material. In this case, the crack failure in the HAZ area will be discussed near the pipe connected to the valve for the heat transfer fluid line. The method used in this paper is the inspection of the attached materials using OES (Optical emission spectroscope), observation of pipe and valve joints and failure analysis. From the results of material inspection, it was found that the pipe used was ASTM A106, then from the microstructure it was seen that the grain dimensions were not homogeneous, it would cause the strength of material heterogeneity, then from visual observation, it could be seen that pipe joints and valve misalignment occurred.
References
A.J. Gaxiola Peralta, dkk., 2013. Effects of welding conditions by TIG and post weld heat treatment in ductile cast iron on the corrosion resistance. Materials Science Forum, 755, hal. 21–27. doi: 10.4028/www.scientific.net/MSF.755.21.
Aloraier, dkk., 2004. Eliminating post-weld heat treatment in repair welding by temper bead technique : role bead sequence in metallurgical changes, Materials Processing Technology, 154, hal. 392–400. doi: 10.1016/j.jmatprotec.2004.04.383.
API, 1998. Inspection Practices for Piping System Components Second edition.
Marko, D., Tomaž, V., Ivan, S. and Dejan, M., 2019. Analysis of heat-affected zone microstructures of steel P92 after welding and after post-weld heat treatment. The International Journal of Advanced Manufacturing Technology, 102(9-12), pp.3801-3812.
Eastman, (2019) Therminol® 66 Heat Transfer Fluid Version 2.5 PRD.
Hyde, T. H. dan Sun, W. 2002. Effect of bending load on the creep failure behaviour of a pressurised thick walled CrMoV pipe weldment, International Journal of Pressure Vessels and Piping, 79, hal. 331–339.
Libyawati, W., Upara, N. dan Suwandi, A. 2019. Analisis Kinematika Pada Desain Alat Bantu Peningkat, A.J. Gaxiola Peralta, dkk., 2013. Effects of welding conditions by TIG and post weld heat treatment in ductile cast iron on the corrosion resistance. Materials Science Forum, 755, hal. 21–27. doi: 10.4028/www.scientific.net/MSF.755.21.
Aloraier, dkk., 2004. Eliminating post-weld heat treatment in repair welding by temper bead technique : role bead sequence in metallurgical changes, Materials Processing Technology, 154, hal. 392–400. doi: 10.1016/j.jmatprotec.2004.04.383.
API, 1998. Inspection Practices for Piping System Components Second edition.
Marko, D., Tomaž, V., Ivan, S. and Dejan, M., 2019. Analysis of heat-affected zone microstructures of steel P92 after welding and after post-weld heat treatment. The International Journal of Advanced Manufacturing Technology, 102(9-12), pp.3801-3812.
Eastman, (2019) Therminol® 66 Heat Transfer Fluid Version 2.5 PRD.
Hyde, T. H. dan Sun, W. 2002. Effect of bending load on the creep failure behaviour of a pressurised thick walled CrMoV pipe weldment, International Journal of Pressure Vessels and Piping, 79, hal. 331–339.
Libyawati, W., Upara, N. dan Suwandi, A. 2019. Analisis Kinematika Pada Desain Alat Bantu Peningkat,
Teknologi, 11(2), hal. 111–116.
Melfi, T., 2010. New code requirements for calculating heat input’, Welding Journal (Miami, Fla), 89(6), hal. 61–63.
Phönix (2010) ‘Bellows Sealed Valves Phönix Product & Order Code’.
Priymak, E., Atamashkin, A. and Stepanchukova, A., 2019. Effect of post-weld heat treatment on the mechanical properties and mechanism of fracture of joint welds made by thompson friction welding. Materials today: proceedings, 11, pp.295-299.
R.C. Mudjianto, dkk., 2019. Analisis Terjadinya Korosi Batas Butir Akibat Proses Pengelasan GTAW Pada Material Austenitic Stainless Steel AISI A304, Jurnal Teknologika, 9(1), hal. 31-37.
Shieddieque, A. D., dkk., 2020. Analysis corrosion resistance and flexural stress of AISI 304L using ER308L in GTAW with currents variations, Technology Reports of Kansai University, 62(6), hal. 3115–3122.
Silva, C. C., dkk., 2009. Welding of ASTM A106 Gr . B steel pipes for high- temperature service – part 1 – residual stress analysis’, Welding International, 23(4), hal. 270–281. doi: 10.1080/09507110802543476.
Smith, E., 1988. The effect of pipe bends on the stability of a circumferential through-wall crack in a type 304 stainless steel piping system’, Engineering Fracture Mechanics, 29(6), hal. 705–712.